Weicon C Aluminum-Filled Liquid Epoxy System is a two-component epoxy resin system developed for repair, casting, and bonding applications that require high temperature resistance. Thanks to its fluid consistency, it can be applied in a controlled manner over large areas, into mold cavities, and onto detailed surfaces. Its aluminum-filled formulation gives the product a metallic character while providing a non-corrosive system that cures with virtually no shrinkage. This Germany-made product is manufactured by WEICON GmbH & Co. KG.<\/p>\n
Technical structure of the Weicon C liquid epoxy system<\/strong> Performance and strength values of the C Aluminum-Filled Epoxy Resin<\/strong> Application method and surface preparation<\/strong> Application areas and key advantages<\/strong> It is an aluminum-filled liquid epoxy resin system. It is used in repair, casting, and bonding applications that require high temperature resistance; with its fluid consistency, it enables controlled application over large areas and delivers durable results.<\/p>\n","protected":false},"featured_media":7057,"comment_status":"open","ping_status":"closed","template":"","meta":[],"product_brand":[326],"product_cat":[291,290],"product_tag":[],"class_list":["post-6460","product","type-product","status-publish","has-post-thumbnail","product_brand-weicon","product_cat-epoxy-resin-systems","product_cat-two-component-adhesives","first","instock","taxable","shipping-taxable","product-type-variable","has-default-attributes"],"_links":{"self":[{"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/product\/6460","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/product"}],"about":[{"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/types\/product"}],"replies":[{"embeddable":true,"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/comments?post=6460"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/media\/7057"}],"wp:attachment":[{"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/media?parent=6460"}],"wp:term":[{"taxonomy":"product_brand","embeddable":true,"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/product_brand?post=6460"},{"taxonomy":"product_cat","embeddable":true,"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/product_cat?post=6460"},{"taxonomy":"product_tag","embeddable":true,"href":"https:\/\/utmteknik.com\/en\/wp-json\/wp\/v2\/product_tag?post=6460"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}
\nThis product is an aluminum-filled epoxy resin system with a fluid character. According to the official technical data sheet, the mixed density is approximately 1.6 g\/cm\u00b3, the consumption at 1 mm layer thickness is around 1.6 kg\/m\u00b2, and the pot life for a 500 g mixture at 20 \u00b0C is approximately 60 minutes. The processing temperature ranges from +15 \u00b0C to +40 \u00b0C, and the product reaches its final strength in about 12 hours at 20 \u00b0C. Technically, it is positioned not only as a filler material, but also as an industrial adhesive and casting-type epoxy system suitable for large-area applications.<\/p>\n
\nWeicon C stands out with its high temperature resistance. The technical documentation specifies a temperature resistance range of -80 \u00b0C to +220 \u00b0C; in addition, its tensile strength is 50 MPa, compressive strength 174 MPa, flexural strength 83 MPa, and Shore D hardness 89 \u00b1 3. The product\u2019s virtually shrinkage-free curing provides an advantage in terms of dimensional stability in large-volume filling and molding applications. These properties make it a strong option especially for industrial bonding, reconstruction, and technical casting applications exposed to thermal loads.<\/p>\n
\nFor successful application, surfaces must be completely free from oil, dirt, rust, oxide, paint, and moisture. The official technical data sheet recommends grinding or, preferably, sandblasting for smooth or heavily contaminated surfaces; a range of 75\u2013100 \u00b5m is recommended for optimum surface roughness. The resin and hardener should be mixed for at least four minutes without entrapping air until a homogeneous mixture is obtained, after which a thin preliminary coat should be worked thoroughly into the surface. Subsequent layers can be added without waiting; the recommended maximum layer thickness in a single application is 10 mm.<\/p>\n
\nThis liquid epoxy system is used for large-area bonding, casting mold cavities, producing fixtures and tools, tooling applications similar to injection molds, and industrial systems exposed to high thermal stress. Its main areas of use include tool and mold manufacturing, machine maintenance and repair, model making, preparation of production fixtures, and metal surface reconstruction. Its ability to penetrate complex geometries thanks to its fluid form, its stability under high temperatures due to its aluminum-filled structure, and its non-magnetic, non-corrosive character are among its key advantages. ISSA and IMPA codes are included in the technical documentation, indicating that the product is classified in the industrial category. In terms of safety, skin and eye contact should be avoided, suitable gloves and eye protection should be used, and work should be carried out in well-ventilated areas.<\/p>\n","protected":false},"excerpt":{"rendered":"